蘇州沖擊改性PBT/PC X4810

詳細內容：型號：PBT/PC X4810 性能：通用級，PBT/PC，礦物，沖擊改性。 XENOY™ Resin X4810 SI | British | Metric | PDF Americas: COMMERCIAL Xenoy X4810 is a hydrostable, High Modulus Ductile PC/PBT blend. This resin provides low temperature (below 0C) ductile impact behaviour, high chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. Xenoy X4810 resin can be considered for body panels, safety equipment, housings, doorhandles, spring-loaded applications, medical device enclosures, outdoor sports equipment. Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 50 mm/min 590 kgf/cm2 ASTM D 638 Tensile Stress, brk, Type I, 50 mm/min 610 kgf/cm2 ASTM D 638 Tensile Stress, yld, Type I, 5 mm/min 560 kgf/cm2 ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 660 kgf/cm2 ASTM D 638 Tensile Strain, yld, Type I, 50 mm/min 4.5 % ASTM D 638 Tensile Strain, brk, Type I, 50 mm/min 150 % ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 4.7 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 150 % ASTM D 638 Tensile Modulus, 5 mm/min 29500 kgf/cm2 ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 940 kgf/cm2 ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 27500 kgf/cm2 ASTM D 790 Taber Abrasion, CS-17, 1 kg 30 mg/1000cy SABIC Method Tensile Stress, yield, 5 mm/min 55 MPa ISO 527 Tensile Stress, break, 5 mm/min 55 MPa ISO 527 Tensile Stress, yield, 50 mm/min 60 MPa ISO 527 Tensile Stress, break, 50 mm/min 55 MPa ISO 527 Tensile Strain, yield, 5 mm/min 4.1 % ISO 527 Tensile Strain, break, 5 mm/min 100 % ISO 527 Tensile Strain, yield, 50 mm/min 4.1 % ISO 527 Tensile Strain, break, 50 mm/min 100 % ISO 527 Tensile Modulus, 1 mm/min 2750 MPa ISO 527 Flexural Stress, yield, 2 mm/min 87 MPa ISO 178 Flexural Modulus, 2 mm/min 2500 MPa ISO 178 Hardness, H358/30 105 MPa ISO 2039-1 IMPACT Value Unit Standard Izod Impact, notched, 23°C 76 cm-kgf/cm ASTM D 256 Izod Impact, notched, 0°C 50 cm-kgf/cm ASTM D 256 Izod Impact, notched, -30°C 15 cm-kgf/cm ASTM D 256 Multiaxial Impact 1121 cm-kgf ISO 6603 Instrumented Impact Total Energy, 23°C 713 cm-kgf ASTM D 3763 Instrumented Impact Total Energy, -20°C 713 cm-kgf ASTM D 3763 Izod Impact, unnotched 80*10*4 +23°C NB kJ/m2 ISO 180/1U Izod Impact, unnotched 80*10*4 -30°C NB kJ/m2 ISO 180/1U Izod Impact, notched 80*10*4 +23°C 50 kJ/m2 ISO 180/1A Izod Impact, notched 80*10*4 0°C 20 kJ/m2 ISO 180/1A Izod Impact, notched 80*10*4 -30°C 12 kJ/m2 ISO 180/1A Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 50 kJ/m2 ISO 179/1eA Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm 15 kJ/m2 ISO 179/1eA Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m2 ISO 179/1eU Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m2 ISO 179/1eU THERMAL Value Unit Standard Vicat Softening Temp, Rate B/50 131 °C ASTM D 1525 HDT, 0.45 MPa, 3.2 mm, unannealed 120 °C ASTM D 648 HDT, 1.82 MPa, 3.2mm, unannealed 98 °C ASTM D 648 CTE, -40°C to 40°C, flow 6.9E-05 1/°C ASTM E 831 CTE, -40°C to 40°C, xflow 8.3E-05 1/°C ASTM E 831 Thermal Conductivity 0.2 W/m-°C ISO 8302 CTE, -30°C to 80°C, flow 8.E-05 1/°C ISO 11359-2 CTE, -30°C to 80°C, xflow 9.E-05 1/°C ISO 11359-2 Vicat Softening Temp, Rate B/50 131 °C ISO 306 Vicat Softening Temp, Rate B/120 133 °C ISO 306 HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 115 °C ISO 75/Bf HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 91 °C ISO 75/Af PHYSICAL Value Unit Standard Specific Gravity 1.25 - ASTM D 792 Mold Shrinkage, flow, 3.2 mm (5) 0.7 - 0.9 % SABIC Method Melt Flow Rate, 266°C/5.0 kgf 12 g/10 min ASTM D 1238 Density 1.25 g/cm3 ISO 1183 Water Absorption, (23°C/sat) 0.42 % ISO 62 Moisture Absorption (23°C / 50% RH) 0.14 % ISO 62 Melt Volume Rate, MVR at 265°C/5.0 kg 10 cm3/10 min ISO 1133 Source GMD, last updated:2006/10/26 Processing Parameter Injection Molding Value Unit Drying Temperature 90 - 100 °C Drying Time 2 - 4 hrs Maximum Moisture Content 0.02 % Melt Temperature 255 - 270 °C Nozzle Temperature 250 - 265 °C Front - Zone 3 Temperature 250 - 270 °C Middle - Zone 2 Temperature 240 - 265 °C Rear - Zone 1 Temperature 230 - 250 °C Hopper Temperature 40 - 60 °C Mold Temperature 60 - 80 °C